HEXAGON FLANGE BOLTS

DIN6921
Material: Aerospace grade Ti alloy 6Al-4V
Finish: Anodised Gold,Blue,Green,Purple and Black
 
Mechanical info about our Ti alloy bolts:
Thread: Rolled thread for better fatigue resistance and
avoid galling,Instead of cut thread
Tensile strength: Heat treated to 950Mpa~1000Mpa
Yield strength: 870Mpa~925Mpa(126,000psi~134,000psi)
Hardness: 30 HRC-40HRC
Shear strength: 500Mpa~550Mpa
Elongation: 14%~18%
Working temp.: Up to 500℃

DIN933

 Standard: DIN933
Material: Aerospace grade Ti alloy 6Al-4V
Finish: Anodised Gold,Blue,Green,Purple and Black
 
Mechanical info about our Ti alloy bolts:
Thread: Rolled thread for better fatigue resistance and
avoid galling,Instead of cut thread
Tensile strength: Heat treated to 950Mpa~1000Mpa
Yield strength: 870Mpa~925Mpa(126,000psi~134,000psi)
Hardness: 30 HRC-40HRC
Shear strength: 500Mpa~550Mpa
Elongation: 14%~18%
Working temp.: Up to 500℃

DIN912

Standard: DIN912
Material: Aerospace grade Ti alloy 6Al-4V
Finish: Anodised Gold,Blue,Green,Purple and Black
 
Mechanical info about our Ti alloy bolts:
Thread: Rolled thread for better fatigue resistance and
avoid galling,Instead of cut thread
Tensile strength: Heat treated to 950Mpa~1000Mpa
Yield strength: 870Mpa~925Mpa(126,000psi~134,000psi)
Hardness: 30 HRC-40HRC
Shear strength: 500Mpa~550Mpa
Elongation: 14%~18%
Working temp.: Up to 500℃

DIN912

Standard: DIN912
Material: Aerospace grade Ti alloy 6Al-4V
Finish: Anodised Gold,Blue,Green,Purple and Black
 
Mechanical info about our Ti alloy bolts:
Thread: Rolled thread for better fatigue resistance and
avoid galling,Instead of cut thread
Tensile strength: Heat treated to 950Mpa~1000Mpa
Yield strength: 870Mpa~925Mpa(126,000psi~134,000psi)
Hardness: 30 HRC-40HRC
Shear strength: 500Mpa~550Mpa
Elongation: 14%~18%
Working temp.: Up to 500℃